Single-component heated-curing epoxy structural adhesive
product description JOME 1767 is a solvent-free one-component epoxy structural adhesive. This product boasts excellent toughness and impact strength. When fully cured through heat, it delivers outstanding bonding performance, electrical conductivity, moisture resistance, and mechanical properties. It demonstrates high adhesion strength to most substrates including glass, metal, and ceramic materials, while meeting stringent requirements for high-temperature bonding and mechanical performance. Widely used in automotive electronics, pressure sensors, wiring harnesses, motor magnet bonding, and inductor fixation applications.
Detailed introduction
Solidify the technical parameters before and after
Item | Test method or condition | JOME 1767 | |
Product code | - | 1767030 | |
Before solidification | Appearance | Measures | Black/white paste |
Viscosity | Rotor 96F,1.5rpm, Pa·s, 25℃ | 260 ± 100 | |
thixotropic index | - | 2.5 | |
flow | mm/1g/90° | ≤20 | |
Density | g/cm3 , 25℃ | 1.65-1.75 | |
After solidification | Hardness | Shore-D, 25℃ | 85 ±5 |
Glass transition temperature Tg | DSC, ℃ | 115 | |
Long term temperature resistance | ℃ | ‒50-180 | |
Cutting strength, iron to iron | MPa, 25℃ | ≥18 | |
impact strength | KJ/m2，25℃ | >6 | |
linear expansion coefficient |
ppm | 40，<Tg 95, >Tg | |
mass resistivity | Ω · cm, DC500V | 1.0 × 1014 | |
Note: 1. The data in the table is the measured data under a certain condition for reference only, and it is not guaranteed that the data obtained by customers in the actual use process can be completely consistent with it
.2. Solidification process: 120℃/1h.
packing specifications
20kg/ plastic barrel, 4kg/ iron barrel, 1kg/ plastic can 30ml per dose in a syringe
Storage and transportation
The storage period of this product is 6 months (<0℃ freezer)
This type of product is non-hazardous and can be transported as a general chemical
| type | model number | Product Description | Color | Viscosity | Complete curing time | Hardness | Thermal conductivity | Usage temperature |
| Single component epoxy | JOME 3621 | High thixotropy, non brushed, high-strength type | grey | Thixotropic paste | 120℃ 1h | 85D | 0.2W | —50~200℃ |
| JOME 3618 | Low viscosity, low-temperature curing | Matte black | 15000cps | 75℃ 30min | 78D | 0.3w | —50~120℃ | |
| JOME 491 | High temperature resistance, high strength | cream-like color | 200000cps | 120℃ 1h | 83D | — | —50~350℃ | |
| JOME 4910 | High temperature resistance, high strength | black | 6600cps | 120℃ 1h | 88D | — | —50~300℃ | |
| JOME 9468 | High transparency | colourless | 550-650cps | 80℃ 30min | 38D | — | —45~150℃ | |
| JOME 7997 | 3.0W high thermal conductivity structural adhesive | grey | 380,000-580,000cps | 150℃ 60min | 85D | 3.0W | —45~150℃ |